316L Stainless Steel Plate
316L stainless steel has a lower proportion of carbon in its composition. To qualify as 316L stainless steel, the amount of carbon cannot exceed 0.03%.
Product Parameters
|
Product Name |
316L Stainless Steel Plate |
|
Type |
Plate |
|
Thickness |
0.3mm-200mm |
|
Length |
2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
|
Width |
40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
|
Standard |
ASTM, AISI, JIS, GB, DIN, EN, etc. |
|
Surface |
BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
|
Scope of Application |
Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
|
Certificate |
ISO, SGS, BV, etc. |
|
Production Technology |
Hot Rolling, Cold Rolling |
|
Edge Processing |
Edging, Trimming |
Chemical Composition
|
C |
Si |
Mn |
Cr |
Ni |
S |
P |
Mo |
|
≤ 0.03 |
≤1.0 |
≤ 2.0 |
16.0～18.0 |
10.0～14.0 |
≤ 0.03 |
≤ 0.045 |
2.0～3.0 |
Mechanical Properties
|
Tensile Strength Kb (MPa) |
Yield Strength σ0.2 (MPa) |
Elongation D5 (%) |
Hardness |
|
≥480 |
≥177 |
≥ 40 |
≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
|
Density(g/cm³) |
Modulus of Elasticity(Gpa) |
Coefficient of Thermal Expansion(10-6/°C) |
Coefficient of Thermal Conductivity(W/m*K) |
Resistivity(ΜΩ. cm) |
|
7.99 |
193 |
16.0 |
16.2 |
74 |
Surface Selection
Related products
-
Contact UsLength : 1.5mm to 70mm
Thickness: 1mm to 50mm
Material grade: The lowest is N35 -
Contact Us304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition with one key difference.
-
Contact UsSize:200mm x 97mm x 40mm
Capacity:700kgs
Net Weight:2.75kg
Material:Stainless steel and NdFeB magnet
Maximum Working Temperature:80°
Package:Carton, 300mm x 210mm x 90mm, 3pcs per carton -
Contact Us304 stainless steel pipe is the most common type of steel pipe across the globe for a number of its characteristics. 304 stainless steel is primarily composed of iron, chromium and nickel. This combination gives rise to outstanding oxidation resistance and corrosion resistance. 304 stainless steel is a versatile stainless steel material with better anti-rust properties than 200 series stainless steel materials. It also outperforms them in high temperature resistance. 304 stainless steel pipe features a smooth surface, high plasticity, toughness and mechanical strength, and is very resistant to corrosion by acids, alkaline gases, solutions and other media. 304 stainless steel pipes are widely used in food processing equipment, building materials, automobile parts and other fields for its versatility and relatively low cost.
-
Contact UsSize: diameter from 1.5-70mm, length from 0.5-100mm. The magnet grade is at least N35.
Information in need: The magnet and the stainless steel grade, size, surface treatment, magnetizing direction, the quantity. Especially when the magnetic force and the temperature are in specific need.
Reviews
There are no reviews yet.